Soda Fired Shop Glaze Tests

Here are some wet glaze blends from the Armory Shop Glazes. Each test was mixed in a small 12 oz styro coffee cup and decanted from already mixed shop glazes with a plastic 60cc  medical syringe. The recipes can be scaled to any amount (for each tile, I mixed about 30cc of glaze).

Recipes Below

Recipes Below

Blend Recipes:

  1. 2 parts Tenmoku/1 Part Angel Eyes/ 1 Part No Man’s Black
  2. 2 Parts Angel Eyes/ 1 Part Tenmoku/ 1 Part Ohata Khaki
  3. 3 Parts Angel Eyes/ 1 Part No Man’s Black
  4. 4 Parts Tenmoku/1 Part Angel Eyes
  5. 4 Parts Angel Eyes/1 Part Tenmoku
  6. 4 Parts No Man’s Black/1 Part Angel Eyes
  7. 2 Parts Ohata Khaki/1 Part Angel Eyes
  8. 2 Parts No Man’s Black/1 Part Angel Eyes/1 Part Tenmoku
  9. 2 Parts Tenmoku/1 Part No Man’s Black
  10. 4 parts Angel Eyes/1 Part Redart Slip
  11. 1 Part No man’s Black/1 Part Angel Eyes/ 1 part Tenmoku
  12. 1 Part No Man’s Black/ I part Ohata Khaki/ I part Angel Eyes

Glaze recipes:

  • Strontium Crystal Magic : Custer Feldspar 40, Calcium Carb 15, Tile 6 Kaolin 12, Strontium Carb. 11, Lithium Carb 4, Frit #3124 4, Bentonite 2| Zinc Oxide .5, Titanium Diox 15
  • No Man’s Black: Kona F-4 Feldspar 524, Dolomite 268, Whiting 184, Kaolin 880, Flint 1048,  Neph Sy 1000, Bentonite 80, Red Iron Oxide 320, Cobalt Carb. 100
  • Tenmoku: G-200 Feldspar 46.5, Whiting 17.4, EpK 10.7, Silica 23.2, Zinc 2.2, Red Iron Ox. 10
  • Ohata Khaki: Custer Feldspar 43.2, Talc 5.6, Whiting 6.4, Bone Ash 8.8, EPK 5.6, Silica 19.2, Red Iron Ox. 9.6
  • Angel Eyes: Custer 40, Whiting 20, EPK 10, Silica 30, Red Iron Ox. 5, Rutile 4
Advertisements

Leave a Reply

Fill in your details below or click an icon to log in:

WordPress.com Logo

You are commenting using your WordPress.com account. Log Out / Change )

Twitter picture

You are commenting using your Twitter account. Log Out / Change )

Facebook photo

You are commenting using your Facebook account. Log Out / Change )

Google+ photo

You are commenting using your Google+ account. Log Out / Change )

Connecting to %s

%d bloggers like this: